UV curable silicone composition and an encapsulant or a sheet film thereof

ABSTRACT

A UV curable silicone composition has exceptional curability by ultraviolet irradiation.The UV curable silicone composition includes(A) an organopolysiloxane composition selected from the following:(A-1) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with alkenyl groups and/or a branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, and an organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain, wherein the thiol group content is 1% by mass or more per molecule,(A-2) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with thiol groups, wherein the thiol group content is 1% by mass or more per molecule, and an organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and/or a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, or(A-3) an organopolysiloxane composition comprising an alkenyl group- and aryl group-containing organopolysiloxane and a multifunctional thiol compound, but furthermore comprising an alkenyl group-containing resinous organopolysiloxane when the multifunctional thiol compound contains only a bifunctional thiol compound, and(B) a silicone-compatible photo-initiator comprising a compound selected from the following:(B-1) an alpha-hydroxyacetophenone,(B-2) a combination of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone, or(B-3) a combination of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide, wherein the ratio between the thiol groups and alkenyl groups (SH/Vi ratio) included in the organopolysiloxane composition is 0.6 or more.

CROSS-REFERENCE TO RELATED APPLICATION

The present application claims priority to and all the benefits of Japanese Application No. 2020-033944 filed on Feb. 28, 2020, which is hereby expressly incorporated herein by reference in its entirety.

DESCRIPTION Technical Field

The present disclosure relates to an ultraviolet curable silicone composition, and to an LED-related member, particularly an encapsulant or a sheet film, that is obtained by curing the ultraviolet curable silicone composition by exposure to ultraviolet rays.

BACKGROUND ART

When curable silicone compositions are cured, they form cured products having excellent heat resistance, cold resistance, electrical insulation, weather resistance, water repellency, and transparency, and are therefore used in a wide range of industrial fields. Compared to other organic materials, the cured products of such curable silicone compositions are less prone to discolouration, with less change in their physical properties, thus making them suitable for optical materials.

However, a problem with conventional thermosetting types of curable silicone compositions is that heating results in a cured product with substantial warping or dimensional errors. In particular, when conventional thermosetting curable types of silicone compositions are used in an attempt to encapsulate flexible substrates on which semiconductor chips have been mounted, or are used as transfer-stamped sheet films in a mass transfer process when chips are being mounted, some potential problems are that heating may result in substantial warping or dimensional errors in the cured product, making it impossible to accurately encapsulate or mount the semiconductor chips. Other potential problems are that thermosetting types of curable silicone compositions must be heated at elevated temperatures for long periods of time in order to be cured, resulting in low processing efficiency or damage to electronic components.

It has therefore been proposed that ultraviolet curable silicone compositions should be used as the curable silicone composition for electronic components such as semiconductor devices. For example, Patent Documents 1 through 8 disclose various ultraviolet curable silicone compositions.

PRIOR ART DOCUMENTS Patent Documents

-   -   [Patent Document 1] Japanese Translation of PCT International         Application Publication No. 2017-502102     -   [Patent Document 2] WO 2013/112254     -   [Patent Document 3] Japanese Translation of PCT International         Application Publication No. 2017-508853     -   [Patent Document 4] Korean Patent 101224780     -   [Patent document 5] Japanese Unexamined Patent Publication No.         2013-253179     -   [Patent document 6] Japanese Unexamined Patent Publication No.         2016-60782     -   [Patent document 7] Japanese Unexamined Patent Publication No.         2002-371261     -   [Patent document 8] Japanese Unexamined Patent Publication No.         2012-144704

SUMMARY OF THE INVENTION Problem to be Solved by the Invention

However, conventional ultraviolet curable silicone compositions still have the problems of poor curability noted above and poor dimensional stability.

An object of the present disclosure is to provide a UV curable silicone composition having exceptional curability by ultraviolet irradiation.

Another object of the present disclosure is to provide a sheet film or encapsulant having exceptional dimensional stability and minimal warping, that is obtained by curing the UV curable silicone composition.

Means for Solving the Problems

As a result of extensive research to solve the above-mentioned problems, the inventors arrived at the present disclosure upon the surprising discovery that a UV curable silicone composition having exceptional curability by ultraviolet irradiation can be obtained by combining a organopolysiloxane composition comprising a specific thiol functional organopolysiloxane, or a specific thiol compound, with a specific photo-initiator.

The present disclosure thus relates to a UV curable silicone composition, comprising:

-   -   (A) an organopolysiloxane composition selected from the         following:         -   (A-1) an organopolysiloxane composition comprising a linear             organopolysiloxane in which both ends of the molecular chain             are capped with alkenyl groups and/or a branched             organopolysiloxane containing at least 2 alkenyl groups at             the ends of the molecular chain, and an organopolysiloxane             containing thiol groups in side-chains of the molecular             chain, wherein the thiol group content is 1% by mass or more             per molecule,         -   (A-2) an organopolysiloxane composition comprising a linear             organopolysiloxane in which both ends of the molecular chain             are capped with thiol groups, wherein the thiol group             content is 1% by mass or more per molecule, and an             organopolysiloxane containing alkenyl groups in side-chains             of the molecular chain and/or a resinous organopolysiloxane             containing at least 2 alkenyl groups at the ends of the             molecular chain, or         -   (A-3) an organopolysiloxane composition comprising an             alkenyl group- and aryl group-containing organopolysiloxane             and a multifunctional thiol compound, but furthermore             comprising an alkenyl group-containing resinous             organopolysiloxane when the multifunctional thiol compound             contains only a bifunctional thiol compound, and     -   (B) a silicone-miscible photo-initiator comprising a compound         selected from the following:         -   (B-1) an alpha-hydroxyacetophenone,         -   (B-2) a combination of an alpha-hydroxyacetophenone and an             alpha-aminoalkylphenone, or         -   (B-3) a combination of an alpha-hydroxyacetophenone and a             mono-acylphosphine oxide, wherein the ratio between the             thiol groups (—SH groups) and alkenyl groups (SH/Vi ratio)             included in the organopolysiloxane composition is 0.6 or             more.

The organopolysiloxane containing at least 2 thiol groups (—SH groups) in side-chains of the molecular chain in component (A-1) is preferably a linear or branched structure.

The organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain in component (A-2) is preferably a linear structure.

The multifunctional thiol compound in component (A-3) is preferably a compound containing 2 to 6 functional thiol groups.

The content of the thiol groups (—SH groups) and alkenyl groups in component (A) of the organopolysiloxane composition is preferably 0.6 to 5 mols thiol groups per mol alkenyl groups.

The photo-initiator (B-1) preferably furthermore contains a compound having an acetophenone structure other than alpha-hydroxyacetophenone.

The content of component (B) is preferably 0.001% by mass to 5% by mass based on the total mass of the UV curable silicone composition.

The present disclosure also relates to an encapsulant or sheet film comprising the cured product of the UV curable silicone composition of the present disclosure.

Effects of the Invention

The UV curable silicone composition according to the present disclosure exhibits exceptional curability by ultraviolet irradiation. A cured product having exceptional dimensional stability and minimal warping can thus be formed. The encapsulant and sheet film according to the present disclosure also have exceptional dimensional stability and minimal warping, thus making it possible to provide highly reliable electronic devices.

MODE FOR CARRYING OUT THE INVENTION

UV Curable Silicone Composition

The UV curable silicone composition according to the present disclosure comprises

-   -   (A) an organopolysiloxane composition selected from the         following:         -   (A-1) an organopolysiloxane composition comprising a linear             organopolysiloxane in which both ends of the molecular chain             are capped with alkenyl groups and/or a branched             organopolysiloxane containing at least 2 alkenyl groups at             the ends of the molecular chain, and an organopolysiloxane             containing thiol groups in side-chains of the molecular             chain, wherein the thiol group content is 1% by mass or more             per molecule,         -   (A-2) an organopolysiloxane composition comprising a linear             organopolysiloxane in which both ends of the molecular chain             are capped with thiol groups, wherein the thiol group             content is 1% by mass or more per molecule, and an             organopolysiloxane containing alkenyl groups in side-chains             of the molecular chain and/or a resinous organopolysiloxane             containing at least 2 alkenyl groups at the ends of the             molecular chain, or         -   (A-3) an organopolysiloxane composition comprising an             alkenyl group- and aryl group-containing organopolysiloxane             and a multifunctional thiol compound, but furthermore             comprising an alkenyl group-containing resinous             organopolysiloxane when the multifunctional thiol compound             contains only a bifunctional thiol compound, and     -   (B) a silicone-miscible photo-initiator comprising a compound         selected from the following:         -   (B-1) an alpha-hydroxyacetophenone,         -   (B-2) a combination of an alpha-hydroxyacetophenone and an             alpha-aminoalkylphenone, or         -   (B-3) a combination of an alpha-hydroxyacetophenone and a             mono-acylphosphine oxide,             wherein the ratio between the thiol groups (—SH groups) and             alkenyl groups (SH/Vi ratio) included in the             organopolysiloxane composition is 0.6 or more.

The components of the UV curable silicone composition of the present disclosure are described in detail below.

(A) Organopolysiloxane Composition

-   -   Component (A) is an organopolysiloxane composition, which is a         main component of the UV curable silicone composition of the         present disclosure. In the present disclosure, component (A) is         selected from the following (A-1) through (A-3):     -   (A-1) an organopolysiloxane composition comprising a linear         organopolysiloxane in which both ends of the molecular chain are         capped with alkenyl groups and/or a branched organopolysiloxane         containing at least 2 alkenyl groups at the ends of the         molecular chain, and an organopolysiloxane containing at least 2         thiol groups in side-chains of the molecular chain, wherein the         thiol group content is 1% by mass or more per molecule,     -   (A-2) an organopolysiloxane composition comprising a linear         organopolysiloxane in which both ends of the molecular chain are         capped with thiol groups, wherein the thiol group content is 1%         by mass or more per molecule, and an organopolysiloxane         containing at least 2 alkenyl groups in side-chains of the         molecular chain and/or a resinous organopolysiloxane containing         at least 2 alkenyl groups at the ends of the molecular chain, or     -   (A-3) an organopolysiloxane composition comprising an alkenyl         group- and aryl group-containing organopolysiloxane and a         multifunctional thiol compound, but furthermore comprising an         alkenyl group-containing resinous organopolysiloxane when the         multifunctional thiol compound contains only a bifunctional         thiol compound. The components are described in detail below.

Component (A-1) is an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with alkenyl groups and/or a branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, and an organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain, wherein the thiol group content is 1% by mass or more per molecule,

The linear organopolysiloxane in which both ends of the molecular chain are blocked with alkenyl groups in component (A-1) is preferably represented by structural formula (I): R¹R² ₂SiO(R² ₂SiO)_(n)SiR¹R² ₂; in formula (I), R¹ is an alkenyl group, R² are each independently a monovalent hydrocarbon group, and n is a numerical value representing a viscosity of 10 mPa or more. Here, 1 kind or combinations of 2 or more kinds of linear organopolysiloxanes in which both ends of the molecular chain are capped with alkenyl groups may be used.

The branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain in component (A-1) is preferably represented by average unit formula (II): (R² ₃SiO_(1/2))_(a)(R² ₂SiO_(2/2))_(b)(R²SiO_(3/2))_(c)(SiO_(4/2))_(d)(XO_(1/2))_(e); in formula (II), R² is the same as the above, but at least 2 of R² among the R² in the unit (R² ₃SiO_(1/2)) are alkenyl groups per molecule, X is a hydrogen atom or an alkyl group, and a, b, c, d, and e are 0≤a≤1.0, 0≤b≤0.5, 0≤c≤0.5, 0≤d≤1.0, and 0≤e<0.4, and a+b+c+d is preferably a value that=1.0. Also, c+d can be >0. One kind or combinations of 2 or more kinds of branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain may be used. In other words, the branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain in component (A-1) contains alkenyl groups in M units. D, T, and/or Q units may contain but preferably do not contain alkenyl groups.

In the present specification, the viscosity of the organopolysiloxane component can be determined at 25° C. using a rotary viscometer per JIS K7117-1.

In the above formulas (I) and (II), R¹ and R² include alkenyl groups. Examples of alkenyl groups include C₂₋₁₂ alkenyl groups such as a vinyl group, an allyl group, a butenyl group, a pentenyl group, a hexenyl group, a heptenyl group, an octenyl group, a nonenyl group, a decenyl group, an undecenyl group, and a dodecenyl group; C₂₋₆ alkenyl groups are preferred, and vinyl groups are particularly preferred.

Examples of monovalent hydrocarbon groups other than alkenyl groups represented by R² in formulas (I) and (II) include C₁₋₁₂ alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl, neopentyl, hexyl, cyclohexyl, heptyl, octyl, nonyl, decyl, undecyl, and dodecyl groups; C₆₋₂₀ aryl groups such as phenyl, tolyl, xylyl, and naphthyl groups; C₇₋₂₀ aralkyl groups such as benzyl, phenethyl, and phenylpropyl groups; and any of these groups in which some or all of the hydrogen atoms are substituted with halogen atoms such as fluorine, chlorine, and bromine atoms; C₁₋₆ alkyl groups are preferred, and methyl groups are particularly preferred. In one embodiment, R² is a monovalent hydrocarbon group other than a phenyl group. In another embodiment, R² is a monovalent hydrocarbon group other than an aryl group.

In component (A-1), the amount of alkenyl groups contained in the linear organopolysiloxane in which both ends of the molecular chain are capped with alkenyl groups is not particularly limited, but alkenyl groups are preferably 0.01 to 50 mol %, 0.03 to 40 mol %, or 0.05 to 32 mol % of the total of functional groups R. The alkenyl group content can be determined by analysis such as Fourier transform infrared spectrophotometry (FT-IR) or nuclear magnetic resonance (NMR).

Examples of the structure of the organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) are linear, linear with some branching, branched, cyclic, and 3D network structures. One kind or combinations of 2 or more kinds of organopolysiloxanes containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) may be used. Component (A-1) preferably comprises an organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain of the linear structure.

The organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain preferably consists only of units M, D, and T among the following general formulas of organopolysiloxanes: siloxane unit (unit M) represented by general formula R³SiO_(1/2),siloxane unit (unit D) represented by general formula R₂SiO_(2/2),siloxane unit (unit T) represented by general formula RSiO_(3/2), and siloxane unit (unit Q) represented by formula SiO_(4/2).

The organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) is preferably represented by average unit formula (III): (R² ₃SiO_(1/2))_(a)(R³ ₂SiO_(2/2))_(b)(R³SiO_(3/2))_(c)(SiO_(4/2))_(d)(XO_(1/2))_(e). In formula (III), R² is the same as above, R³ is a monovalent hydrocarbon group or thiol group other than an alkenyl group, but at least 2 of R³ are thiol groups per molecule, X is a hydrogen atom or alkyl group, a, b, c, d, and e are 0≤a≤1.0, 0≤b≤1.0, 0≤c<0.9, 0≤d<0.5, and 0≤e<0.4, and a+b+c+d is preferably a value that=1.0.

In formula (III), R³ is a monovalent hydrocarbon group or thiol group other than an alkenyl group; examples of monovalent hydrocarbon groups other than alkenyl groups are the same as for the monovalent hydrocarbon groups represented by R². Examples of thiol groups include the structure —(CH₂)_(x) SH, where x is an integer of 1 to 30. Preferred examples of alkyl groups represented by X include C₁₋₃ alkyl groups, specifically, methyl, ethyl, and propyl groups.

In formula (III), a is preferably in the range of 0≤a≤0.9, more preferably in the range of 0≤a≤0.7, and ideally in the range of 0≤a≤0.5. In formula (III), b is preferably in the range of 0.1≤b≤1.0, more preferably in the range of 0.3≤b≤1.0, and particularly in the range of 0.5≤b≤1.0. In formula (III), c is preferably in the range of 0≤c≤0.5, more preferably in the range of 0≤c≤0.3, and particularly in the range of 0≤c≤0.1. In formula (III), d is preferably in the range of 0≤d≤0.4, more preferably in the range of 0≤d≤0.2, and particularly in the range of 0≤d≤0.1. In formula (III), e is preferably in the range of 0≤e≤0.3, more preferably 0≤e≤0.2, and particularly in the range of 0≤e≤0.1.

The amount of the thiol groups contained in the organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) is 1% by mass or more, and preferably 1.2% by mass or more, and is, for example, no more than 30% by mass, and preferably no more than 25% by mass. The thiol group content (% by mass) can be calculated, for example, as the % by mass of thiol groups per molecular weight.

The amount of organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) is not particularly limited, but can be, based on the total mass of component (A-1), 0.1% by mass or more, 0.3% by mass or more, or 0.5% by mass or more, and can be no more than 90% by mass, no more than 85% by mass, and no more than 80% by mass.

Component (A-2) is an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with thiol groups, wherein the thiol group content is 1% by mass or more per molecule, and an organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and/or a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain.

The linear organopolysiloxane in which both ends of the molecular chain are blocked with thiol groups in component (A-2) is preferably represented by structural formula (IV): R⁴R⁵ ₂SiO(R⁵ ₂SiO)_(p)SiR⁴R⁵ ₂; in formula (IV), R⁴ is a thiol group, R⁵ are each independently a monovalent hydrocarbon group other than an alkenyl group, and p is a numerical value representing a viscosity of 10 mPa or more. Here, 1 kind or combinations of 2 or more kinds of linear organopolysiloxanes in which both ends of the molecular chain are capped with thiol groups may be used.

In formula (IV), R⁴ is a thiol group, for example, a thiol group represented by the structure —(CH₂)_(x)—SH (x is an integer of 1 to 30).

The amount of thiol groups per molecule contained in the linear organopolysiloxane in which both ends of the molecular chain are capped with thiol groups in component (A-2) is 1% by mass or more, and preferably 1.2% by mass or more, and is, for example, no more than 30% by mass, and preferably no more than 25% by mass. The thiol group content (% by mass) can be calculated, for example, as the % by mass of thiol groups per molecular weight.

Component (A-2) comprises an organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and/or a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain.

Examples of the structure of the organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain in component (A-2) are linear, linear with some branching, branched, cyclic, and 3D network structures. One kind or combinations of 2 or more kinds of organopolysiloxanes containing at least 2 alkenyl groups in side-chains of the molecular chain in component (A-2) may be used. Component (A-2) preferably comprises a linear organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain.

The organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain in component (A-2) is preferably represented by average unit formula (V): (R⁵ ₃SiO_(1/2))_(a)(R² ₂SiO_(2/2))_(b)(R²SiO_(3/2))_(c)(SiO_(4/2))_(a)(XO_(1/2))_(e). In formula (V), R⁵ is the same as above, R² is a monovalent hydrocarbon group, but at least 2 of R² are alkenyl groups per molecule, X is a hydrogen atom or alkyl group, a, b, c, d, and e are 0≤a≤1.0, 0≤b≤1.0, 0≤c<0.9, 0≤d<0.5, and 0≤e<0.4, and a+b+c+d is a value that=1.0.

In formula (V), R² is a monovalent hydrocarbon group, including an alkenyl group; examples of alkenyl groups are the same as for R¹, and examples of monovalent hydrocarbon groups are the same as for R². Examples of thiol groups include the structure —(CH₂)_(x) SH, where x is an integer of 1 to 30. Preferred examples of alkyl groups represented by X include C₁₋₃ alkyl groups, specifically, methyl, ethyl, and propyl groups.

In formula (V), a is preferably in the range of 0≤a≤0.9, more preferably in the range of 0≤a≤0.7, and ideally in the range of 0≤a≤0.5. In formula (V), b is preferably in the range of 0.1≤b≤1.0, more preferably in the range of 0.3≤b≤1.0, and particularly in the range of 0.5≤b≤1.0. In formula (V), c is preferably in the range of 0≤c≤0.5, more preferably 0c≤0.3, and particularly in the range of 0c≤0.1. In formula (V), d is preferably in the range of 0≤d≤0.4, more preferably in the range of 0≤d≤0.2, and particularly in the range of 0≤d≤0.1. In formula (V), e is preferably in the range of 0≤e≤0.3, more preferably 0≤e≤0.2, and particularly in the range of 0≤e≤0.1.

The organopolysiloxane containing at least 2 alkenyl groups in side-chains of molecular chain in component (A-2) is preferably linear, and is therefore preferably represented by structural formula (VI): R⁵ ₃SiO(R² ₂SiO)_(q)SiR⁵ ₃. Here, in formula (VI), R² is the same as above, R⁵ is the same as above but at least 2 of R² are alkenyl groups per molecule, and q is a viscosity in the range of 10 mPas or more.

Component (A-2) can contain a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain. In the present specification, resinous organopolysiloxanes refer to organopolysiloxanes that have a branched or network molecular structure. In one embodiment, the molecular structure of the resinous organopolysiloxane that can be included in component (A-2) contains at least one siloxane unit (T unit) represented by RSiO_(3/2) and/or siloxane unit (Q unit) represented by SiO_(4/2).

The resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain in component (A-2) is preferably represented by average unit formula (VII): (R² ₃SiO_(1/2))_(a)(R² ₂SiO_(2/2))_(b)(R²SiO_(3/2))_(c)(SiO_(4/2))_(a)(XO_(1/2))_(e); in formula (VII), R² is a monovalent hydrocarbon group, but at least 2 of R² among R² in the unit (R² ₃SiO_(1/2)) are alkenyl groups per molecule, X is a hydrogen atom or an alkyl group, and a, b, c, d, and e are 0≤a≤1.0, 0≤b≤1.0, 0≤c≤0.9, 0≤d≤1.0, and 0≤e≤0.4, a+b+c+d=1.0, and c+d>0). Preferably, in the resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain in component (A-2), alkenyl groups are present only in unit M, and units D, T, and/or Q contain no alkenyl groups. Examples of alkenyl groups represented by R² are the same as for R¹, and examples of monovalent hydrocarbon groups are the same as for R². Preferred examples of alkyl groups represented by X include C₁₋₃ alkyl groups, specifically, methyl, ethyl, and propyl groups.

In component (A-2), the amount of alkenyl groups contained in the organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and the resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain is not particularly limited, but alkenyl groups are, for example, preferably 0.01 to 50 mol %, 0.05 to 40 mol %, or 0.09 to 32 mol % of the total of functional groups R. The alkenyl group content can be determined by analysis such as Fourier transform infrared spectrophotometry (FT-IR) or nuclear magnetic resonance (NMR).

In component (A-2), the amount of the organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular structure and/or the resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain is not particularly limited, but can be 10% by mass or more, 20% by mass or more, 30% by mass or more, 40% by mass or more, or 50% by mass or more, and can be no more than 90% by mass, no more than 85% by mass, or no more than 80% by mass, based on the total mass of component (A-2).

Component (A-3) is an organopolysiloxane composition comprising an alkenyl group- and aryl group-containing organopolysiloxane and a multifunctional thiol compound.

Examples of the structure of the alkenyl group- and aryl group-containing organopolysiloxane in component (A-3) are linear, linear with some branching, branched, cyclic, and 3D network structures. One kind or combinations of 2 or more kinds of alkenyl group- and aryl group-containing organopolysiloxanes in component (A-3) may be used. Component (A-3) preferably comprises a linear alkenyl group- and aryl group-containing organopolysiloxane.

The alkenyl group- and aryl group-containing organopolysiloxane in component (A-3) is preferably represented by average unit formula (VII): (R² ₃SiO_(1/2))_(a)(R² ₂SiO_(2/2))_(b)(R²SiO_(3/2))_(c)(SiO_(4/2))_(a)(XO_(1/2))_(e). In formula (VII), R² is, in the same manner as above, a monovalent hydrocarbon group, including alkenyl groups, but at least 2 of R² are alkenyl groups, and at least 1 of R² is an aryl group, per molecule, X is a hydrogen atom or alkyl group, a, b, c, d, and e are 0≤a≤1.0, 0≤b≤1.0, 0≤c<0.9, 0≤d≤1.0, and 0≤e<0.4, a+b+c+d=1.0.

In formula (VII), R⁵ is a monovalent hydrocarbon group, including an alkenyl group; examples of alkenyl groups are the same as for R¹, and examples of monovalent hydrocarbon groups are the same as for R² or R⁵. Aryl groups are preferably phenyl groups. Preferred examples of alkyl groups represented by X include C₁₋₃ alkyl groups, specifically, methyl, ethyl, and propyl groups.

The aryl groups of the alkenyl group- and aryl group-containing organopolysiloxane in component (A-3) may be contained at either the ends of the molecular chain or in side-chains of the molecular chain, but are preferably contained in side-chains of the molecular chain, and more preferably only in side-chains of the molecular chain. The alkenyl groups of the alkenyl group- and aryl group-containing organopolysiloxane in component (A-3) may be contained at either the ends of the molecular chain or in side-chains of the molecular chain.

The alkenyl group- and aryl group-containing organopolysiloxane in component (A-3) is preferably linear, and is therefore preferably represented by structural formula (VIII): R⁷R⁶ ₂SiO(R⁸ ₂SiO)_(r)SiR⁶ ₂R⁷. Here, in formula (VIII), R⁶ through R⁸ are each independently monovalent hydrocarbon groups, including alkenyl groups, but at least 2 of R⁶ through R⁸ are alkenyl groups and at least 1 is an aryl group per molecule, and r is a viscosity in the range of 10 mPas or more.

In formula (VIII), examples of alkenyl groups represented by R⁶ through R⁸ are the same as for R¹, and examples of monovalent hydrocarbon groups are the same as for R² or R⁵. In a preferred embodiment, R⁷ is an alkenyl group, R⁷ are each independently monovalent hydrocarbon groups other than alkenyl groups, and R⁸ is a monovalent hydrocarbon group other than an alkenyl group, but at least one R⁸ is an aryl group, and preferably a phenyl group, per molecule.

In component (A-3), the amount of alkenyl groups contained in the alkenyl group- and aryl group-containing organopolysiloxane is not particularly limited, but alkenyl groups are, for example, preferably 0.01 to 50 mol %, 0.05 to 40 mol %, or 0.1 to 30 mol % of the total of functional groups R. The alkenyl group and aryl group content can be determined by analysis such as Fourier transform infrared spectrophotometry (FT-IR) or nuclear magnetic resonance (NMR).

The multifunctional thiol compound in component (A-3) is a compound containing 2 or more thiol groups per molecule. The multifunctional thiol compound may also contain tertiary thiol groups.

Examples of multifunctional thiol compounds include, but are not particularly limited to, bifunctional to hexafunctional primary or secondary thiol compounds. The multifunctional thiol compound is preferably at least a trifunctional thiol compound.

Examples of bifunctional secondary thiol compounds include 1,4-bis (3-mercaptobutyryloxy) butane, bis (1-mercaptoethyl) phthalate, bis (2-mercaptopropyl) phthalate, bis (3-mercaptobutyl) phthalate, ethylene glycol bis (3-mercaptobutyrate), propylene glycol bis (3-mercaptobutyrate), diethylene glycol bis (3-mercaptobutyrate), butanediol bis (3-mercaptobutyrate), octanediol bis (3-mercaptobutyrate), ethylene glycol bis (2-mercaptopropionate), propylene glycol bis (2-mercaptopropionate), diethylene glycol bis (2-mercaptopropionate), butanediol bis (2-mercaptopropionate), octanediol bis (2-mercaptopropionate), ethylene glycol bis (2-mercaptopropionate), propylene glycol bis (2-mercaptopropionate), diethylene glycol bis (2-mercaptopropionate), butanediol bis (2-mercaptopropionate), octanediol bis (2-mercaptopropionate), ethylene glycol bis (4-mercaptovalerate), propylene glycol bis (4-mercaptoisovalerate), diethylene glycol bis (4-mercaptovalerate), butanediol bis (4-mercaptovalerate), octanediol bis (4-mercaptovalerate), ethylene glycol bis (3-mercaptovalerate), propylene glycol bis (3-mercaptovalerate), diethylene glycol bis (3-mercaptovalerate), butanediol bis (3-mercaptovalerate), and octanediol bis (3-mercaptovalerate.

Examples of trifunctional secondary thiol compounds include trimethylolpropane tris (3-mercaptobutyrate), trimethylolpropane tris (2-mercaptopropionate), trimethylolpropane tris (2-mercaptopropionate), trimethylolpropane tris (4-mercaptovalerate), trimethylolpropane tris (3-mercaptovalerate), 1,3,5-tris (3-mercaptobutyloxyethyl)-1,3,5-triazine-2,4,6 (1H, 3H, 5H)-trione.

Examples of tetrafunctional secondary thiol compounds include dipentaerythritol hexakis (3-mercaptobutyrate), pentaerythritol tetrakis (2-mercaptopropionate), pentaerythritol tetrakis (3-mercapto-2-propionate), pentaerythritol tetrakis (2-mercaptoisobutyrate), pentaerythritol tetrakis (4-mercaptovalerate), pentaerythritol and tetrakis (3-mercaptovalerate).

Examples of hexafunctional secondary thiol compounds include dipentaerythritol hexakis (3-mercaptobutyrate), dipentaerythritol hexakis (2-mercaptopropionate), dipentaerythritol hexakis (2-mercaptoisobutyrate), dipentaerythritol hexakis (4-mercaptovalerate), and dipentaerythritol hexakis (3-mercaptovalerate).

An example of a bifunctional primary thiol compound is 2,2′-(ethylenedioxy)diethanethiol.

An example of a trifunctional primary thiol compound is trimethylolpropane tris (3-mercaptopropionate).

An example of a tetrafunctional primary thiol compound is pentaerythritol tetrakis (3-mercaptopropionate).

In preferred embodiments, the multifunctional thiol compound contains no hydroxyl groups.

When component (A-3) contains only a bifunctional thiol compound as the multifunctional thiol compound, an alkenyl group-containing resinous organopolysiloxane is included as an organopolysiloxane component in the interests of curability. Examples of such alkenyl group-containing resinous organopolysiloxanes include the same as for the “alkenyl group-containing resinous organopolysiloxanes” noted in the “additional components” section below.

The molecular weight of the multifunctional thiol compound is not particularly limited but can be, for example, 100 or more, 120 or more, or 150 or more, and no more than 10,000, no more than 5,000, no more than 4,000, no more than 3,000, or no more than 2,000.

The amount of the multifunctional thiol compound in component (A-3) is not particularly limited, but can be, based on the total mass of component (A-3), 0.1% by mass or more, 0.3% by mass or more, or 0.5% by mass or more, and can be no more than 90% by mass, no more than 70% by mass, or no more than 50% by mass.

Additional Components

The organopolysiloxane composition of component (A) may further contain, in addition to the above components, an alkenyl group-containing resinous organopolysiloxane. For example, the organopolysiloxane composition of component (A-1) and/or (A-3) may further contain, in addition to the above components, an alkenyl group-containing resinous organopolysiloxane.

In one embodiment of the present disclosure, the resinous organopolysiloxane that can be included in component (A) is preferably represented by average unit formula (IX): (R² ₃SiO_(1/2))_(a)(R² ₂SiO_(2/2))_(b)(R²SiO_(3/2))_(c)(SiO_(4/2))_(a)(XO_(1/2))_(e); in formula (IX), R² is a monovalent hydrocarbon group, but at least 2 of R² are alkenyl groups per molecule, X is a hydrogen atom or an alkyl group, and a, b, c, d, and e are 0≤a≤1.0, 0≤b≤1.0, 0≤c<0.9, 0≤d≤1.0, and 0≤e<0.4, a+b+c+d=1.0, and c+d>0. Examples of alkenyl groups represented by R² are the same as for R¹, and examples of monovalent hydrocarbon groups are the same as for R². Preferred examples of alkyl groups represented by X include C₁₋₃ alkyl groups, specifically, methyl, ethyl, and propyl groups.

In average unit formula (IX), a is preferably in the range of 0≤a≤0.9, more preferably in the range of 0≤a≤0.8, and particularly in the range of 0≤a≤0.7. In average unit formula (IX), b is preferably in the range of 0≤b≤0.9, more preferably in the range of 0≤b≤0.7, and particularly in the range of 0≤b≤0.5. In average unit formula (IX), c is preferably in the range of 0c≤0.9, more preferably in the range of 0≤c≤0.85, and particularly in the range of 0c≤0.8. In average unit formula (IX), d is preferably in the range of 0≤d≤0.9, more preferably in the range of 0≤d≤0.8, even more preferably in the range of 0≤d≤0.7. In average unit formula (IX), e is preferably in the range of 0≤e≤0.3, more preferably in the range of 0≤e≤0.2, and particularly in the range of 0≤e≤0.1.

The alkenyl group content in the resinous organopolysiloxane that can be included in component (A) (mol % of alkenyl groups in all silicon atom-bonded functional groups of the resinous organopolysiloxane) can be designed as desired, but should be 0.5 mol % or more, preferably 1 mol % or more, more preferably 1 mol % or more, and even more preferably 2 mol % or more, and can be 40 mol % or less, preferably 35 mol % or less, more preferably 30 mol % or less, and preferentially 25 mol % or less. The alkenyl group content can be determined by analysis such as Fourier transform infrared spectrophotometry (FT-IR) or nuclear magnetic resonance (NMR).

The content of the resinous organopolysiloxane that can be included in component (A) is not particularly limited, but can be 1% by mass or more, preferably 3% by mass or more, and more preferably 5% by mass or more, based on the total mass of organopolysiloxane composition (A). The content of the resinous organopolysiloxane that can be included in component (A) can be 70% by mass or less, preferably 60% by mass or less, and more preferably 50% by mass or less, based on the total mass of organopolysiloxane composition (A).

The ratio between the thiol groups (—SH groups) and alkenyl groups (SH/Vi ratio) in the organopolysiloxane composition (A) is not particularly limited, but is preferably 0.6 to 5 mols, and preferably 0.7 to 3 mols thiol groups per mol alkenyl group. The amount of alkenyl groups can be calculated based on vinyl groups (Vi groups).

The ratio between the thiol groups and alkenyl groups (SH/Vi ratio) included in the organopolysiloxane composition of the present disclosure is 0.6 or more. Here, the amount of alkenyl groups can be calculated based on vinyl groups (Vi groups). The ratio between the thiol groups and alkenyl groups (SH/Vi ratio) included in the organopolysiloxane composition of the present disclosure is 0.7 or more, and more preferably 0.8 or more. [0079] (B) Silicone-miscible photo-initiator The UV curable silicone composition of the present disclosure comprises a silicone-miscible photo-initiator as component (B). Here, “miscible” refers to the property of the photo-initiator being completely mixed with the organopolysiloxane composition of component (A). For example, as used in the present specification, “silicone-miscible” means the property of 1 g/100 mL or more being dissolved in silicone oil.

The silicone-miscible photo-initiator of component (B) comprises the following:

-   -   (B-1) an alpha-hydroxyacetophenone,     -   (B-2) a combination of an alpha-hydroxyacetophenone and an         alpha-aminoalkylphenone, or     -   (B-3) a combination of an alpha-hydroxyacetophenone and a         mono-acylphosphine oxide.         -   The components are described in detail below.

Examples of alpha-hydroxyacetophenone (B-1) include 2-hydroxy-2-methyl-1-phenyl-1-propanone (by IGM Resins B. V.; brand name: Omnirad 1173); 2-hydroxy-4′(2-hydroxyethoxy)-2-methylpropiophenone (by IGM Resins B. V.; brand name Omnirad 2959), oligo-[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)-phenyl]-propanone], 1,1′-(methylene-di-4,1-phenylene) bis [2-hydroxy-2-methyl-1-propanone](by IGM Resins B. V.; brand name: Omnirad 127D), and 1-hydroxycyclohexyl-phenylketone (by IGM Resins B. V.; brand name: Omnirad 184).

The photo-initiator (B-1) may furthermore contain a compound having an acetophenone structure other than alpha-hydroxyacetophenone in addition to the alpha-hydroxyacetophenone. Examples of compounds having such an acetophenone structure include, but are not particularly limited to, 4-phenoxydichloroacetophenone, 4-t-butyldichloroacetophenone, 4-t-butyltrichloroacetophenone, and diethoxyacetophenone.

In a particularly preferred embodiment, the alpha-hydroxyacetophenone-containing photo-initiator (B-1) contains only alpha-hydroxyacetophenone and either contains no other photo-initiator or contains another photo-initiator in an amount 10% by mass or less, 5% by mass or less, or 3% by mass or less based on the total mass of component (B).

Examples of alpha-aminoalkylphenones in (B-2) combinations of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone include 2-methyl-1-[4-(methylthio)phenyl]-2-(4-morpholinyl)-propan-1-one (by IGM Resins B. V.; brand name: Omnirad 907), 2-dimethylamino-2-(4-methylbenzyl)-1-(4-morpholin-4-yl-phenyl)-butan-1-one (by IGM Resins B. V.; brand name: Omnirad 379EG), 2-benzyl-2-dimethylamino-1-(3,4-dimethoxy-phenyl)-butan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholin-4-yl-phenyl)-butan-1-one, 2-(dimethylamino)-1-(4-morpholinophenyl)-2-benzyl-1-butanone (by IGM Resins B. V.; brand name: Omnirad 369), and 2-methyl-1-(4-methylsulfanyl-phenyl)-2-morpholin-4-yl-propan-1-one.

The weight ratio between the alpha-hydroxyacetophenone and alpha-aminoalkylphenone in (B-2) combinations of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone is not particularly limited, but the mass ratio of the alpha-hydroxyacetophenone to the alpha-aminoalkylphenone may be, for example, 0.1 to 100, preferably 0.5 to 50, and more preferably 1 to 20.

In a particularly preferred embodiment, a photo-initiator comprising (B-2) a combination of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone will consist of only an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone, and will either contain no other photo-initiator or contain another photo-initiator in an amount 10% by mass or less, 5% by mass or less, or 1% by mass or less based on the total mass of component (B).

Examples of mono-acylphosphine oxides in (B-3) combinations of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide include (2,4,6-trimethylbenzoyl)-diphenyl-phosphine oxide (by IGM Resins B. V.; brand name: Omnirad TPO-H) and phenyl-(2,4,6-trimethylbenzoyl)-phosphinate ethyl ester (by IGM Resins B. V.; brand name: Omnirad TPO-L).

The weight ratio between the alpha-hydroxyacetophenone and mono-acylphosphine oxide in (B-3) combinations of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide is not particularly limited, but the mass ratio of the alpha-hydroxyacetophenone to the mono-acylphosphine oxide may be, for example, 0.1 to 100, preferably 0.5 to 50, and more preferably 0.8 to 20.

In a particularly preferred embodiment, the photo-initiator comprising (B-3) a combination of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide will consist of only an alpha-hydroxyacetophenone and a mono-acylphosphine oxide, and will either contain no other photo-initiator or contain another photo-initiator in an amount 10% by mass or less, 5% by mass or less, or 1% by mass or less based on the total mass of component (B).

In the present specification, examples of “other photo-initiators” include, but are not limited to, photo-initiators other than those listed as components of (B-1) through (B-3), such as bisacylphosphine oxides, trisacylphosphine oxides, phenyl glyoxalates, thioxanthone, benzoin ethers, and oxime ester. The photo-initiator (B) of the present disclosure need not include some of these other photo-initiators. The photo-initiator (B) of the present disclosure may either include no photo-initiator other than an alpha-hydroxyacetophenone, alpha-aminoalkylphenone, or mono-acylphosphine oxide, or may contain them in an amount 10% by mass or less, 5% by mass or less, or 1% by mass or less, based on the total mass of component (B).

The content of the photo-initiator (B) is not particularly limited, but is preferably, based on the total mass of the UV curable silicone composition, 0.001% by mass or more, more preferably 0.01% by mass or more, even more preferably 0.1% by mass or more, preferentially 1% by mass or more, and in particular preferably 2% by mass or more. In a preferred embodiment, the content of the photo-initiator (B) is 10% by mass or less, more preferably 5% by mass or less, and even more preferably 3% by mass or less, based on the total mass of the UV curable silicone composition.

Optional components can be blended into the UV curable silicone composition of the present disclosure, provided that the object of the present disclosure is not thereby compromised. Examples of optional components include amino group-containing siloxane compounds, glycidyl (epoxy) group-containing siloxane compounds, ionic liquids, acetylene compounds, organic phosphorus compounds, vinyl group-containing siloxane compounds, ultraviolet absorbers, sensitizers, photostabilizers, free radical scavengers, polymerization inhibitors, antioxidants, ultraviolet absorbers, antifoaming agents, leveling agents, inorganic fillers, surfactants, coupling agents, tackifiers, mold release agents, metal soaps, agents that impart heat resistance, agents that impart cold resistance, thermally conductive fillers, agents that impart flame retardance, agents that impart thixotropic properties, fluorescent substances, and solvents.

Examples of polymerization inhibitors (also referred to as a free radical scavengers) that can be used include, but are not particularly limited to, alkoxy-titanium or the following products: Genorad (registered trademark) 16, Genorad (registered trademark) 24 (the above are by Rahn AG); Sumilizer (registered trademark) GA-80, Sumilizer (registered trademark) GM, Sumilizer (registered trademark) GS (the above are by Sumitomo Chemical); Irgastab (registered trademark) UV10, Irgastab (registered trademark) UV22, Tinuvin (registered trademark) 460, Tinuvin (registered trademark) CGS20 (the above are by Ciba Specialty Chemicals); Floorstab (registered trademark) UV (UV-1, UV-2, UV-5, UV-8) (by Kromachem); and Additor (registered trademark) S (S100, S110, S120, S130) (by Cytec Surface Specialties).

The UV curable silicone composition of the present disclosure can be prepared by mixing the components. The method of mixing the components may be a conventionally known method, and is not particularly limited, and a uniform mixture is usually obtained by simple mixing. When solid components such as inorganic filler are included as an optional component, it is preferable to use a mixing device for the mixing. There are no particular limitations regarding this mixing device, and examples include single- and twin-screw continuous mixers, double roller mixers, Ross mixers, Hobart mixers, dental mixers, planetary mixers, kneader mixers, Henschel mixers, and the like.

Use in the Form of Encapsulant and Sheet Film

The present disclosure also relates to an encapsulant or sheet film obtained by curing the UV curable silicone composition of the present disclosure. The sheet film of the present disclosure is preferably used as an encapsulant layer or an adhesive sheet film for mass transfer, and is obtained by curing the UV curable silicone composition of the present disclosure, resulting in exceptional dimensional stability and minimal warping. Preferred examples of electronic devices for which the sheet film of the present disclosure may used include, but are not particularly limited to, optical semiconductor devices, such as light emitting diodes (LED), semiconductor lasers, photodiodes, phototransistors, solid-state imaging, and light emitters and light receivers photocouplers.

The encapsulant or sheet film of the present disclosure can be obtained, for example, by coating a base material in the form of a film, tape, or sheet with the UV curable silicone composition of the present disclosure, which is then cured by irradiation with ultraviolet rays to form a cured film on the surface of the base material. The thickness of the cured film is not particularly limited but preferably ranges from 1 μm to 10 mm or from 5 μm to 5 mm.

In the present specification, the term “ultraviolet” refers to electromagnetic radiation having a wavelength of about 10 nm to about 400 nm, and the wavelength for ultraviolet curing can be selected from, for example, UVA and UVB wavelength bands at 280 nm to 400 nm. Examples of devices that generate ultraviolet rays include high-pressure mercury lamps, medium-pressure mercury lamps, and ultraviolet LEDs. The level of ultraviolet ray exposure is not particularly limited but, at 365 nm, should be preferably 1 to 1,000 mW/cm², more preferably 5 to 500 mW/cm², and even more preferably 10 to 200 mW/cm².

EXAMPLES

The UV curable silicone composition of the present disclosure is described in greater detail by means of the following examples and comparative examples.

The starting material components shown below were used in the following examples and comparative examples. Below, Me represents a methyl group, Vi represents a vinyl group, and Ph represents a phenyl group.

-   -   Component a-1-1: Linear organopolysiloxane in which both ends of         the molecular chain are capped with vinyl groups, which is         represented by general formula ViMe₂ SiO(Me₂SiO)₃₁₀SiMe₂Vi     -   Component a-1-2: Linear organopolysiloxane in which both ends of         the molecular chain are capped with vinyl groups, which is         represented by general formula ViMe₂ SiO(Me₂SiO)₁₅₀SiMe₂Vi     -   Component a-1-3: Linear organopolysiloxane in which both ends of         the molecular chain are capped with vinyl groups, which is         represented by general formula ViMe₂ SiO(Me₂SiO)₅₃₀SiMe₂Vi     -   Component a-1-4: Linear organopolysiloxane in which both ends of         the molecular chain are capped with vinyl groups, which is         represented by general formula ViMe₂ SiO(Me₂SiO)₇₇₀SiMe₂Vi     -   Component a-1-5: Linear organopolysiloxane in which both ends of         the molecular chain are capped with vinyl groups, which is         represented by general formula ViMe₂SiO(Me₂SiO)_(n)SiMe₂Vi,         wherein the viscosity is 60 mPas, and the vinyl group content is         1.5 mol %     -   Component a-2-1: Linear organopolysiloxane having a vinyl group         in a side-chain of the molecular chain, which is represented by         unit formula Me₃SiO(MeViSiO)_(n)(Me₂SiO)_(m)SiMe₃, wherein the         viscosity is 35000 mPas, and the alkenyl group content is 0.5 wt         %     -   Component a-2-2: Linear organopolysiloxane having a vinyl group         in a side-chain of the molecular chain, which is represented by         unit formula Me₃SiO(MeViSiO)_(n)(Me₂SiO)_(m)SiMe₃, wherein the         viscosity is 8000 mPas, and the vinyl group content is 0.3 wt %     -   Component a-2-3: Linear organopolysiloxane having vinyl groups         at the ends of, and in a side-chain of, the molecular chain,         which is represented by unit formula         ViMe₂SiO(MeViSiO)_(n)(Me₂SiO)_(m)SiMe₂Vi, wherein the viscosity         is 370 cSt, and the vinyl group content is 1.1 wt %     -   Component a-2-4:         1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane     -   Component a-2-5: Branched alkenyl group-containing         organopolysiloxane represented by (ViMe₂SiO)₃(PhSiO_(3/2))     -   Component a-3-1: Organopolysiloxane containing a thiol group in         a side-chain of the molecular chain, which is represented by         unit formula (Me₂SiO)_(n)(HSMeSiO)_(m), wherein the viscosity is         100 mPas, and the thiol group content is 3.6 wt %     -   Component a-3-2: Organopolysiloxane containing a thiol group in         a side-chain of the molecular chain, which is represented by         unit formula (Me₂SiO)_(n)(HSMeSiO)_(m), wherein the viscosity is         150 mPas, and the thiol group content is 4.6 wt %     -   Component a-3-3: Organopolysiloxane containing a thiol group in         a side-chain of the molecular chain, which is represented by         unit formula (Me₂SiO)_(n)(HSMeSiO)_(m), wherein the viscosity is         150 mPas, and the thiol group content is 1.5 wt %     -   Component a-3-4: Organopolysiloxane containing a thiol group in         a side-chain of the molecular chain, which is represented by         unit formula (HSMeSiO)_(n), wherein the viscosity is 100 mPas,         and the thiol group content is 23 wt %     -   Component a-3-5: Organopolysiloxane containing a thiol group in         a side-chain of the molecular chain, which is represented by         unit formula (Me₂SiO)_(n)(HSMeSiO)_(m), wherein the viscosity is         150 mPas, and the thiol group content is 0.8 wt %     -   Component a-4-1: Linear organopolysiloxane in which both ends of         the molecular chain are capped with thiol groups, which is         represented by unit formula HSMe₂SiO(Me₂SiO)_(n)SiMe₂SH, wherein         the viscosity is 90 mPas, and the thiol group content is 1.4 wt         %     -   Component a-4-2: Linear organopolysiloxane in which both ends of         the molecular chain are capped with thiol groups, which is         represented by unit formula HSMe₂SiO(Me₂SiO)_(n)SiMe₂SH, wherein         the viscosity is 55 mPas, and the thiol group content is 2.0 wt         %     -   Component a-5-1: Phenyl group-containing linear         organopolysiloxane in which both ends of the molecular chain are         capped with vinyl groups, which is represented by general         formula ViMe₂ SiO(PhMeSiO)₂₀SiMe₂Vi     -   Component a-5-2: Phenyl group-containing linear         organopolysiloxane in which both ends of the molecular chain are         capped with vinyl groups, which is represented by general         formula ViMe₂ SiO(Me₂ SiO)₂₀₀(Ph₂SiO)₅₀SiMe₂Vi     -   Component a-5-3: Phenyl group-containing linear         organopolysiloxane in which both ends of the molecular chain are         capped with vinyl groups, which is represented by general         formula ViMe₂ SiO(Me₂ SiO)₆₀(Ph₂SiO)₃₀SiMe₂Vi     -   Component a-6-1: Resinous vinyl group-containing         organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₄(Me₃SiO_(1/2))₄₀(SiO_(4/2))₅₆     -   Component a-6-2: Resinous vinyl group-containing         organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₁₁(Me₃SiO_(1/2))₃₄(SiO_(4/2))₅₅     -   Component a-6-3: Resinous vinyl group-containing         organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₁₅(Me₃SiO_(1/2))₄₅(SiO_(4/2))₄₀     -   Component a-6-4: Resinous vinyl group-containing         organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₁₀(Me₃SiO_(1/2))₄₀(SiO_(4/2))₅₀     -   Component a-6-5: Resinous vinyl group- and phenyl         group-containing organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₂₅(PhSiO_(3/2))₇₅     -   Component a-6-6: Resinous vinyl group- and phenyl         group-containing organopolysiloxane represented by unit formula         (ViMe₂SiO_(1/2))₁₅(Me₂SiO_(2/2))₃₅(PhSiO_(3/2))₅₀     -   Component a-6-7: Resinous vinyl group- and phenyl         group-containing organopolysiloxane represented by unit formula         (ViMeSiO_(2/2))₂₅(Ph₂SiO_(2/2))₃₅(PhSiO₃/2)₄₅     -   Component a-7-1: Trifunctional secondary thiol compound         represented by compositional formula C₁₈H₃₂O₆S₃         trimethylolpropane tris (3-mercaptobutyrate)     -   Component a-7-2: Bifunctional primary thiol compound represented         by compositional formula HSCH₂CH₂OCH₂CH₂OCH₂CH₂SH         2,2′-(ethylenedioxy) diethanethiol.     -   Component a-7-3: Bifunctional primary thiol compound represented         by compositional formula (HSCH₂COOCH₂)₂ ethylene glycol         bismercaptoacetate     -   Component a-7-4: Trifunctional primary thiol compound         represented by composition formula (HSCH₂CH₂CO₂CH₂)₃CC₂H₅         trimethylolpropane tris (3-mercaptopropionate)     -   Component a-7-5: Tetrafunctional primary thiol compound         represented by composition formula (HSCH₂CH₂COOCH₂)₄C         pentaerythritol tetrakis (3-mercaptopropionate)     -   Component a-7-6: Bifunctional secondary thiol compound         represented by compositional formula C₁₂H₂₂O₄S₂ 1,4-bis         (3-mercaptobutyryloxy) butane     -   Component a-7-7: Trifunctional primary thiol compound         represented by compositional formula C₁₈H₂₇N₃O₉S₃ tris         [2-(3-mercaptopropionyloxy)ethyl]isocyanurate     -   Component a-7-8: Trifunctional secondary thiol compound         represented by compositional formula C₂₁H₃₃O₉N₃S₃ 1,3,5-tris         (2-(3-sulfanylbutanoyloxy) ethyl)-1,3,5-triazinane-2,4,6-trione     -   Component a-7-9: Tetrafunctional secondary thiol compound         represented by compositional formula C₂₁H₃₆O₈S₄ pentaerythritol         tetrakis (3-mercaptobutyrate)     -   Component b-1: 2-hydroxy-2-methyl-1-phenyl-1-propanone (by IGM         Resins B. V.; brand name: Omnirad 1173)     -   Component b-2: 1,1′-(methylene-di-4,1-phenylene) bis         [2-hydroxy-2-methyl-1-propanone] (by IGM Resins B. V.; brand         name: Omnirad 127D)     -   Component b-3: 1-hydroxycyclohexyl-phenylketone (by IGM         Resins B. V.; brand name: Omnirad 184)     -   Component b-4:         2-methyl-1-[4-(methylthio)phenyl]-2-(4-morpholinyl)-propan-1-one         (by IGM Resins B. V.; brand name: Omnirad 907)     -   Component b-5:         2-dimethylamino-2-(4-methylbenzyl)-1-(4-morpholin-4-yl-phenyl)-butan-1-one         (by IGM Resins B. V.; brand name: Omnirad 379EG)     -   Component b-6: Phenyl-(2,4,6-trimethylbenzoyl)-phosphinate ethyl         ester (by IGM Resins B. V.; brand name: Omnirad TPO-L).     -   Component b-7: 2,4,6-trimethylbenzoyl)-diphenyl-phosphine oxide         (by IGM Resins B. V.; brand name: Omnirad TPO-H).     -   Component b-8:         2-benzyl-2-(dimethylamino)-4′-morpholinobutyrophenone (by IGM         Resins B. V.; brand name: Omnirad 369)     -   Component b′-1: Methyl benzoylformate (by IGM Resins B. V.;         brand name: Omnirad MBF)     -   Component b′-2: 2,4-diethylthioxanthen-9-one (DETX)     -   Component b′-3: phenyl bis (2,4,6-trimethylbenzoyl)-phosphine         oxide (by IGM Resins B. V.; brand name: Omnirad 819)     -   Component b′-4: Ethyl 4-(dimethylamino)benzoate (by IGM         Resins B. V.; brand name: Omnirad EDB)     -   Component b′-5: 1,1′-(oxybis(4,1-phenylene))bis         (2-hydroxy-2-methylpropan-1-one (by LEHVOSS; brand name: Esacure         KIP160)     -   Component b′-6:         1-[4-(4-benzoylphenylsulfanyl)phenyl]-2-methyl-2-(4-methylphenylsulfonyl)propan-1-one         (by LEHVOSS; brand name: Esacure E1001M)     -   Component b′-7: Thioxanthone-based photo-initiator (by LEHVOSS;         brand name: Esacure One)     -   Component b′-8: (4,4′-bis(diethylamino)benzophenone (by IGM         Resins B. V.; brand name: Omnirad EMK)     -   Component b′-9: Polybutylene glycol bis(4-benzoylphenoxy)acetate         (by IGM Resins B. V.; brand name: Omnipol BP)     -   Component b′-10: 2,2-dimethoxy-2-phenylacetophenone (by IGM         Resins B.I.V.; brand name: Omnirad 651)     -   Component c: Photo-sensitizer Anthracure (registered trademark)         UVS-1331 (by Kawasaki Kasei Chemicals Ltd.)

Examples 1-53 and Comparative Examples 1-34

UV silicone compositions were prepared by mixing the respective components in the proportions (% by mass) shown in Tables 1 through 9. The “SH/Vi ratio” in the tables indicates the molar ratio between the thiol groups and vinyl groups in the organopolysiloxane components.

EVALUATION

The curability of the compositions in the examples and comparative examples was determined as shown below, and the results are shown in Tables 1 through 9.

The resulting compositions were applied with the use of a blade coater to a thickness of 10 m on PET films. Films were obtained by curing the compositions via ultraviolet light irradiation as described in (1) through (3) below using a metal halide lamp.

-   -   (1) Wavelength 254 nm; 5.4 mJ/cm² (irradiation for 1 min)     -   (2) Wavelength 365 nm; 12.3 J/cm² (irradiation for 1 min)     -   (3) Wavelength 405 nm; 69.3 J/cm² (irradiation for 1 min)

The resulting films were cut to a size of 5×5 cm², the resulting cut samples were dipped in 50 mL of toluene, washed for 30 minutes, and then dried for 90 minutes at 120° C., and the residual weight was determined. The residual weight values that were determined are shown in Tables 1 through 5 below. Compositions having a residual weight of 50% or more can be assessed as having exceptional curability. “Not mixed” indicates compositions in which components (A) and (B) could not be mixed, and “not cured” indicates compositions that could not be cured.

TABLE 1 Example Example Example Example Example Example Example Example Example Example Component 1 2 3 4 5 6 7 8 9 10 a-1-1 90.7 90.7 90.7 90.7 90.7 90.7 90.7 90.7 42 28.8 a-2-1 — — — — — — — — — — a-3-1 8.3 8.3 8.3 8.3 8.3 8.3 8.3 8.3 24 46 a-6-1 — — — — — — — — 33 22.7 b-1 1 0.875 0.67 0.66 0.91 0.5 0.8 0.91 1 2.5 b-2 — 0.125 — — — — — — — — b-3 — — 0.33 — — — — — — — b-4 — — — 0.33 — — — — — — b-5 — — — — 0.09 — — — — — b-6 — — — — — 0.5 — — — — b-7 — — — — — — 0.2 — — — b-8 — — — — — — — 0.09 — — Total 100 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 0.9 2.54 ratio Evaluation Residual 50 51 55 55 60 55 66 60 60 80 weight (%)

TABLE 2 Example Example Example Example Example Example Example Example Example Example Example Component 11 12 13 14 15 16 17 18 19 20 21 a-1-1 — — 46.5 — — — 8.4 23.2 90.7 42 81.5 a-1-2 84 — — — — — — — — — — a-1-3 — 93.8 — — 41.3 — — — — — — a-1-4 — — 46.5 — — 30 66 20 — — — a-1-5 — — — 60 — — — — — — — a-3-1 15 5.2 6.0 39 33.4 43 — — — — — a-3-2 — — — — — — — — 8.3 24 — a-3-3 — — — — — — — — — — 17.5 a-4-1 — — — — — — 18 37.5 — — — a-6-1 — — — — — — 6.6 18.3 — 33 — a-6-2 — — — — 24.3 — — — — — — a-6-3 — — — — — 26 — — — — — b-1 1 1 1 1 1 1 1 1 1 1 1 Total 100 100 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 0.9 0.9 1.0 1.0 1.5 1.1 1.2 ratio Evaluation Residual 55 50 50 83 75 55 50 54 90 95 50 weight (%)

TABLE 3 Example Example Example Example Example Example Example Example Example Example Component 22 23 24 25 26 27 28 29 30 31 a-1-1 97.6 — — — — — — — — — a-1-2 — — — — — — — — 13.1 — a-1-3 — 41.4 — — — — — 14.6 — — a-1-5 — — — — — — 10.2 — — — a-3-1 — — — — — — 49 44 45.5 — a-3-3 — 30 — — — — — — — — a-3-4 1.4 3.2 — — — — — — — — a-5-1 — — — — — — — — — 90.5 a-5-2 — — 97.6 — — 71 — — — — a-5-3 — — — 96 94.9 — — — — — a-6-2 — 24.3 — — — — — — — — a-6-3 — — — — — 19 — — — — a-6-4 — — — — — 1 39.8 40.4 40.4 — a-7-1 — — 1.4 — — 8 — — — — a-7-4 — — — — — — — — — 8.5 a-7-8 — — — — 4.1 — — — — — a-7-9 — — — 3 — — — — — — b-1 1 1 1 1 1 1 1 1 1 1 Total 100 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 1.3 1.0 0.9 0.9 1.2 ratio Evaluation Residual 50 77 60 65 60 61 72 72 70 60 weight (%)

TABLE 4 Example Example Example Example Example Example Example Example Example Example Component 32 33 34 35 36 37 38 39 40 41 a-1-1 — — — — 29.7 26.3 — — — — a-1-4 — — — — — 10 — — — — a-2-4 — 20 — — — — — — — — a-2-5 — — — 41 — — — — — — a-4-1 — — — — 46 42 — — — — a-5-1 90.5 34 62.5 15 — — 93 62.5 62.5 62.5 a-6-1 — — — — 23.3 20.7 — — — — a-6-5 — — 22.5 — — — — 22.5 — — a-6-6 — — — — — — — — 22.5 — a-6-7 — — — — — — — — — 22.5 a-7-1 — 45 14 43 — — 6 — 14 14 a-7-2 — — — — — — — 14 — — a-7-5 8.5 — — — — — — — — — b-1 1 1 1 1 1 1 1 1 1 1 Total 100 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.0 0.9 1.0 0.8 1.2 1.5 1.3 ratio Evaluation Residual 65 88 68 84 54 59 60 60 71 59 weight (%)

TABLE 5 Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- ple ple ple ple ple ple ple ple ple ple ple ple Component 42 43 44 45 46 47 48 49 50 51 52 53 a-1-1 42 28.8 42 28.8 — — — — — — — — a-2-1 — — — — 65 — — 71 — — — — a-2-2 — — — — — 75 — — — — — — a-2-3 — — — — — — 47 — — — — — a-3-1 24 46 24 46 — — — — — — — — a-4-1 — — — — 34 24 52 — — — — — a-4-2 — — — — — — — 28 — — — — a-5-1 — — — — — — — — 90.5 90.5 90.5 90.5 a-6-1 33 22.7 33 22.7 — — — — — — — — a-7-1 — — — — — — — — 8.5 8.5 8.5 8.5 b-1 0.91 2.27 0.8 2 1 1 1 1 1 0.66 0.91 0.8 b-4 — — — — — — — — — 0.33 — — b-5 0.09 0.23 — — — — — — — — 0.09 — b-7 — — 0.2 0.5 — — — — — — — 0.2 Total 100 100 100 100 — — — — — — — — SH/Vi 0.9 2.54 0.9 2.54 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 ratio Evaluation Residual 70 95 67 85 65 55 72 61 67 66 66 65 weight (%)

TABLE 6 Comparative Comparative Comparative Comparative Comparative Comparative Comparative Comparative Comparative Example Example Example Example Example Example Example Example Example Component 1 2 3 4 5 6 7 8 9 a-1-1 90.7 90.7 90.7 90.7 90.7 90.7 95 90 — a-3-1 8.3 8.3 8.3 8.3 8.3 8.3 4 — — a-3-3 — — — — — — — 9 — a-5-1 — — — — — — — — 95 a-7-1 — — — — — — — — 4 b-1 — — 0.5 — 0.75 — 1 1 1 b-7 1 — — — — — — — — b′-1 — 1 0.5 0.99 — 0.91 — — — b′-2 — — — — 0.25 — — — — b′-3 — — — — — 0.09 — — — c — — — 0.01 — — — — — Total 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 1.2 0.55 0.55 0.55 ratio Evaluation Residual 40 20 20 20 20 40 40 30 20 weight (%)

TABLE 7 Comparative Comparative Comparative Comparative Comparative Comparative Comparative Comparative Example Example Example Example Example Example Example Example Component 10 11 12 13 14 15 16 17 a-1-1 90.7 90.7 90.7 90.7 90.7 90.7 90.7 90.7 a-3-1 8.3 8.3 8.3 8.3 8.3 8.3 8.3 8.3 b-1 — — 0.91 — — — — — b-7 — — — — — — — 1 b′-4 1 — — — — — — — b′-5 — 1 — — — — — — b′-6 — — 0.09 — — — — — b′-7 — — — 1 — — — — b′-8 — — — — 1 — — — b′-9 — — — — — 1 — — b′-10 — — — — — — 1 — Total 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 ratio Evaluation State Not Not Not Not Not Not Not Not mixed mixed mixed mixed mixed mixed mixed mixed

TABLE 8 Compar- Compar- Compar- Compar- Compar- Compar- Compar- Compar- Compar- Compar- Compar- Compar- ative ative ative ative ative ative ative ative ative ative ative ative Compo- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- Exam- nent ple 18 ple 19 ple 20 ple 21 ple 22 ple 23 ple 24 ple 25 ple 26 ple 27 ple 28 ple 29 a-5-1 90.5 90.5 90.5 90.5 90.5 96 90.5 90.5 90.5 90.5 90.5 90.5 a-7-1 8.5 8.5 8.5 8.5 8.5 3 — — — — — — a-7-6 — — — — — — 8.5 8.5 8.5 27 — — a-7-7 — — — — — — — — — — — 8.5 a-7-8 — — — — — — — — — 8.5 — — a-7-9 — — — — — — — — — — 8.5 — b-1 — 0.91 — — — — 1 — — — — — b-6 — — — — — — — 1 — — — — b-7 — — — — 1 1 — — — — — — b′-1 — — — — — — — — 0.91 — — — b′-3 — — — — — — — — 0.09 — — — b′-5 1 — — — — — — — — — — — b′-6 — 0.09 — — — — — — — — — — b′-7 — — 1 — — — — — — — — — b′-8 — — — 1 — — — — — — — — Total 100 100 100 100 100 100 100 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 0.4 1.2 1.2 1.2 1.2 1.2 1.2 ratio Evaluation State Not Not Not Not Not Not Not Not Not Not Not Not mixed mixed mixed mixed mixed cured cured cured cured mixed mixed mixed

TABLE 9 Comp- Comp- Comp- Comp- Comp- arative arative arative arative arative Example Example Example Example Example Component 30 31 32 33 34 a-1-1 — — 69 — — a′-3-5 — — 30 — — a-5-1 90.5 90.5 — 90.5 90.5 a-7-1 — — — 8.5 8.5 a-7-2 8.5 — — — — a-7-3 — 8.5 — — — b-1 1 1 1 — — b′-9 — — — 1 — b′-10 — — — — 1 Total 100 100 100 100 100 SH/Vi 1.2 1.2 1.2 1.2 1.2 ratio Evaluation Residual Not Not 30 Not Not weight cured cured mixed mixed (%)

The above results show that the UV curable silicone compositions of Examples 1 through 53 of the present disclosure had exceptional UV irradiation curability. The UV curable silicone compositions of the present disclosure thus

INDUSTRIAL APPLICABILITY

The UV curable silicone composition of the present disclosure is particularly useful in providing encapsulants for electronic devices, particularly optical semiconductor devices such as light emitting diodes (LEDs), semiconductor lasers, photodiodes, phototransistors, solid-state imaging, and light emitters and light receivers for photocouplers, as well as adhesive sheet films for mass transfer. 

The invention claimed is:
 1. An encapsulant for an optical semiconductor that is a cured product of curable silicone composition comprising: (A) an organopolysiloxane composition selected from the following; (A-1) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with alkenyl groups and/or a branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, and an organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain, wherein the thiol group content is 1% by mass or more per molecule, (A-2) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with thiol groups, wherein the thiol group content is 1% by mass or more per molecule, and an organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and/or a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, or (A-3) an organopolysiloxane composition comprising an alkenyl group- and aryl group-containing organopolysiloxane and a multifunctional thiol compound, provided that component (A-3) comprises an alkenyl group-containing resinous organopolysiloxane when the multifunctional thiol compound contains only a bifunctional thiol compound, and (B) a silicone-miscible photo-initiator comprising a compound selected from the following: (B-1) an alpha-hydroxyacetophenone, (B-2) a combination of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone, or (B-3) a combination of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide, wherein the mole ratio between the thiol groups (—SH) and alkenyl groups (—SH/Vi ratio) included in the organopolysiloxane composition is 0.6 or more.
 2. An adhesive sheet film that is a cured product of curable silicone composition comprising: (A) an organopolysiloxane composition selected from the following; (A-1) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with alkenyl groups and/or a branched organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, and an organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain, wherein the thiol group content is 1% by mass or more per molecule, (A-2) an organopolysiloxane composition comprising a linear organopolysiloxane in which both ends of the molecular chain are capped with thiol groups, wherein the thiol group content is 1% by mass or more per molecule, and an organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain and/or a resinous organopolysiloxane containing at least 2 alkenyl groups at the ends of the molecular chain, or (A-3) an organopolysiloxane composition comprising an alkenyl group- and aryl group-containing organopolysiloxane and a multifunctional thiol compound, provided that component (A-3) comprises an alkenyl group-containing resinous organopolysiloxane when the multifunctional thiol compound contains only a bifunctional thiol compound, and (B) a silicone-miscible photo-initiator comprising a compound selected from the following: (B-1) an alpha-hydroxy acetophenone, (B-2) a combination of an alpha-hydroxyacetophenone and an alpha-aminoalkylphenone, or (B-3) a combination of an alpha-hydroxyacetophenone and a mono-acylphosphine oxide, wherein the mole ratio between the thiol groups (—SH) and alkenyl groups (—SH/Vi ratio) included in the organopolysiloxane composition is 0.6 or more.
 3. An encapsulant for optical semiconductor as claimed in claim 1, wherein the organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) is a cyclic structure.
 4. An encapsulant for optical semiconductor as claimed in claim 1, wherein the organopolysiloxane containing at least 2 thiol alkenyl groups in side-chains of the molecular chain in component (A-2) is a linear structure.
 5. An encapsulant for optical semiconductor as claimed in claim 1, wherein the photo-initiator of (B-1) further comprises a compound having an acetophenone structure other than alpha-hydroxyacetophenone.
 6. An encapsulant for optical semiconductor as claimed in claim 1, wherein the content of component (B) is 0.001% by mass to 5% by mass based on the total mass of the UV curable silicone composition.
 7. An adhesive sheet film as claimed in claim 2, wherein the organopolysiloxane containing at least 2 thiol groups in side-chains of the molecular chain in component (A-1) is a cyclic structure.
 8. An adhesive sheet film as claimed in claim 2, wherein the organopolysiloxane containing at least 2 alkenyl groups in side-chains of the molecular chain in component (A-2) is a linear structure.
 9. An adhesive sheet film as claimed in claim 2, wherein the photo-initiator of (B-1) further comprises a compound having an acetophenone structure other than alpha-hydroxyacetophenone.
 10. An adhesive sheet film as claimed in claim 2, wherein the content of component (B) is 0.001% by mass to 5% by mass based on the total mass of the UV curable silicone composition. 